Abstract
The influence of Y 2 O 3 , Pr 2 O 3 , Nd 2 O 3 , Sm 2 O 3 and Yb 2 O 3 coatings on Fe-30Cr alloy oxidation behaviour was investigated at 1000°C in air under atmospheric pressure. Isothermal exposures indicated that the Y 2 O 3 coating was the most protective after 100 hours. Pr 2 O 3 , Nd 2 O 3 and Sm 2 O 3 coatings were less effective, but the less beneficial effect was observed when Yb 2 O 3 coating was applied onto the Fe-Cr alloy surface. Two-stage oxidation experiments in 16 O 2 and then 18 O 2 were performed to get information about the chromia growth phenomena with and without reactive elements. The 18 O-tracer distribution was determined by secondary ion mass spectrometry (SIMS) and sputtered neutral mass spectrometry (SNMS). The experiments performed on uncoated samples clearly demonstrated that chromia growth mechanism was controlled by chromium cationic diffusion, whereas on reactive element coated samples the external diffusion of chromium ions was not predominant.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.