Abstract
The AISI 300M ultra-high strength steel was applied for the automotive suspension coil spring. Recently, some premature failures were reported, which caused by synergistic effect of cyclic mechanical stress and corrosion, namely corrosion fatigue cracking. In this study, the accurate mechanism of corrosion fatigue cracking for coil spring steel was studied for the proper prevention method against the catastrophic failure. Fatigue life was evaluated in 5 wt% NaCl solution under the anodic dissolution and hydrogen embrittlement conditions, which is simulated by applying constant potentials. Scanning electron microscopy and energy dispersive X-ray spectroscopy analysis indicated that the corrosion fatigue cracking was initiated at the MnS inclusion of the pit initiation site. The calculation of hydrogen production corresponding to each corrosion fatigue test condition revealed the two operating mechanisms of the cracking process. The corrosion fatigue cracking failure of coil spring steel was mainly caused by the anodic dissolution combined with hydrogen embrittlement.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.