Abstract
Chitosan (CS) hollow fiber (HF) membranes were successfully prepared according to the dry–wet spinning technique. A post-treatment with glutaraldehyde (GA) aqueous solution was carried out to perform the cross-linking reaction. The effect of GA concentration in the range 50–1000mgl−1 on the swelling, mechanical and adsorptive properties was investigated. The morphology and chemical structure of the fibers were examined by means of SEM and FTIR. The degree of swelling and adsorption capacity decreased as the GA concentration increased. CS hollow fibers swelled the most in acidic solution as compared with distilled water and saline solution. The adsorption capacity of CS HFs increased while decreasing of initial pH from 7.5 to 3.5. Desorption experiments showed that CS HFs were reusable as adsorbent. Mechanical properties were strongly affected by GA post-treatment: tensile strength and elastic modulus increased at low GA concentration (50mgl−1), to sharply decrease when concentration was ⩾500mgl−1. Breaking elongation decreased with increasing GA concentration.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.