Abstract
Bi1.84Pb0.34Sr2.03Ca1.9Cu3.06Oy, bulk superconductors were prepared by hot press sintering at 800°C at a pressure range from 50 kgf/cm2 to 200 kgf/cm2 in air for 2 h. The relative density increased with increasing the hot-pressing pressure, and specimens with various relative densities of 70%–90% were prepared. The flexural strength (σ) at room temperature was related to the porosity (p) as follows: σ = 138 exp(−2.83 p) (MPa). The flexural strengths of the specimen with p = 0.1 were 103 MPa and 113 MPa at room temperature and at 83 K, respectively. The flexural strength tended to increase with decreasing temperature. Anisotropy in flexural strength was observed, which seemed to be due to the grain-oriented microstructure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.