Abstract
The formation of intermetallic compounds in brazed joints between SUS304 and nickel-based filler metal is a major concern, since they considerably degrade the mechanical properties of joints. In this study, the SUS304, which is used widespread, as a general material was vacuum brazed with BNi-2 filler metal, and discussed to determine the influence of different brazing temperature and time on the strength of brazed joints. The results showed that, the mechanical properties of brazing layer could be stabilized through increasing the brazing temperature over 100° C more than melting temperature of filler metal, and increasing the brazing time over 120min. long, and diffusing enough the intermetallic compounds formed in the brazing layer to the base metal.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.