Abstract
1. Annealing of hot-rolled steel Kh15N5D2T at 580–700°C leads to the α→γ transformation, accompanied by higher plasticity. 2. After normalization and low-temperature aging the steel is strengthened as the result of the martensitic transformation and the precipitation of excess intermetallic phase.