Abstract
Plate impact experiment has been carried out on Al 2024-T4 alloy using single stage gas gun. The dynamic yield strength and spall strength of Al 2024-T4 sample has been determined to be 0.35 GPa and 1.43 GPa, respectively, from free surface velocity history measured using VISAR. The sample recovered after unloading from peak shock pressure of 4.4 GPa along with an unshocked sample is analyzed for mechanical properties using nano-indentation and scanning electron microscopy (SEM). The nano-indentation measurements reveal that the hardness and Young's modulus for unshocked sample remains unchanged as a function of load (equivalently depth), however, the same for shocked sample decreases monotonically with increase of load up to ∼40 mN and on further increase of load it remains unchanged, suggesting the (i) increase in hardness of shock loaded sample; (ii) the increase in hardness is limited to certain depth, which in our case is 845.12 ± 43.16 nm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.