Abstract
In this paper, carbon fibre fabric reinforced polymeric composites with the capability of self-healing were studied. These fabric-composite laminates were fabricated by hand lay-up of plain weave (PW) carbon fibre fabrics impregnated with polymer blends of epoxy resin and thermoplastic healing agent. Laminates containing different amounts of healing agent (0, 10wt% and 20wt% by weight of epoxy) were evaluated by tensile and three-point flexural tests according to the ASTM D3039/D3039M and D790, respectively. Aside of the potential for self-healing, benefits were found in terms of tensile and flexural properties. Overall, tensile properties were improved with addition of thermoplastic healing agent; the highest tensile strength and failure strain were obtained with the highest healing agent amount (20wt%) whilst the maximum tensile modulus was obtained at 10wt%. In general, flexural properties were also improved except flexural strain; the highest flexural strength and modulus were determined at 10wt%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.