Abstract
In this study, B4C-TiB2 ceramic composites were manufactured by hot pressing method. The raw materials for the in-situ synthesis of TiB2 were TiO2 and TiC. After being sintered at 1900°C for 60min under a pressure of 30MPa, compact composites samples with a TiB2 volume fraction range from 0 to 11.05% were prepared. The relative density, fracture toughness and flexural strength of different sample were tested. Microstructures on the fracture surface were studied by SEM. The result shows that B4C-TiB2 ceramic composites sintered from B4C-TiC had a better mechanical property than the one sintered from B4C-TiO2. When the content of TiB2 (reacted from TiC) was 11.05vol.%, the strength and toughness of B4C-TiB2 ceramics can reach 598MPa and 6.45MPa·m1/2. The toughening mechanisms of B4C-TiB2 composites include micro-crack toughening and energy consumption by the pulling out process of second phase.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.