Abstract
Consolidation of cordierite disc specimens was undertaken under concentrated solar beam in a solar furnace at PSA (Plataforma Solar de Almeria). Satisfactory extent of densification was achieved by the present solar-sintering experiment. The mechanical properties measured for the solar-sintered cordierite test pieces were; density p = 2.45 ± 0.02 g/cm 3 , Vickers microhardness HV = 7.31 ± 0.29 GPa, Young's modulus E = 97 ± 5 GPa, shear modulus G = 38 ± 2 GPa, Poisson ratio ν = 0.27 ± 0.01, fracture toughness K IC = 1.50 ± 0.15 MPa·m 1/2 and modulus of rupture evaluated by ring-on-ring test MOR ROR =57.8± 13.7MPa which were comparable to those of the counterparts sintered by conventional industrial gas furnace.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.