Abstract
The mechanical, metallurgical and corrosion properties of Alloy 625 produced using the laser powder bed fusion (L-PBF) manufacturing process were investigated and compared with typical performance of the alloy produced using conventional forging processes. Test specimens were produced near net shape along with several demonstration pieces that were produced to examine the geometric complexity that could be achieved with the process. The additively manufactured specimens exhibited strength, fracture toughness and impact toughness that was equal to or better than properties typically achieved for wrought product. There was no evidence of stress corrosion cracking susceptibility in 3.5% NaCl solution at stress intensities up to 70 ksi-in1/2 after 700h exposure. The microstructure was equiaxed in the plane of the powder bed build platform (X–Y) and exhibited a columnar shape in the Z direction although there was not any significant evidence of anisotropy in the mechanical properties.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.