Abstract

A study has been systematically made of the effect of bainite on the mechanical properties of a commercial Japanese 0.40 pct C-Ni-Cr-Mo high strength steel (AISI 4340 type) having a mixed structure of martensite and bainite. Isothermal transformation of lower bainite at 593 K, which appeared in acicular form and partitioned prior austenite grains, in association with tempered marprovided provided a better combination of strength and fracture ductility, improving true notch tensile strength (TNTS) and fracture appearance transition temperature (FATT) in Charpy impact tests. This occurred regardless of the volume fraction of lower bainite present and/or the tempering conditions employed to create a difference in strength between the two phases. Upper bainite which was isothermally transformed at 673 K appeared as masses that filled prior austenite grains and had a very detrimental effect on the strength and fracture ductility of the steel. Significant damage occurred to TNTS and FATT, irrespective of the volume fraction of upper bainite present and/or the tempering conditions employed when the upper bainite was associated with tempered martensite. However, when the above two types of bainite appeared in the same size, shape, and distribution within tempered martensite approximately equalized to the strength of the bainite, a similar trend or a marked similarity was observed between the tensile properties of the mixed structures and the volume fraction of bainite. From the above results, it is assumed that the mechanical properties of high strength steels having a mixed structure of martensite and bainite are affected more strongly by the size, shape, and distribution of bainite within martensite than by the difference in strength between martensite and bainite or by the type of mixed bainite present. The remarkable effects of the size, shape, and distribution of bainite within martensite on the mechanical properties of the steel are briefly discussed in terms of the modified law of mixtures, metallographic examinations, and the analyses of stress-strain diagrams.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call