Mechanical properties, corrosion behavior, and in vitro and in vivo biocompatibility of hot-extruded Zn-5RE (RE = Y, Ho, and Er) alloys for biodegradable bone-fixation applications

Abstract

Biodegradable Zn alloys have significant application potential for hard-tissue implantation devices owing to their suitable degradation behavior and favorable biocompatibility. Nonetheless, pure Zn and its alloys in the as-cast state are mechanically instable and low in strength, which restricts their clinical applicability. Here, we report the exceptional mechanical, corrosion, and biocompatibility properties of hot-extruded Zn-5RE (wt.%, RE = rare earth of Y; or Ho; or Er) alloys intended for use in biodegradable bone substitutes. The microstructural characteristics, mechanical behavior, corrosion resistance, cytocompatibility, osteogenic differentiation, and capacity of osteogenesis in vivo of the Zn-5RE alloys are comparatively investigated. The Zn-5Y alloy demonstrates the best tensile properties, encompassing a 138 MPa tensile yield strength, a 302 MPa ultimate tensile strength, and 63% elongation, while the Zn-5Ho alloy shows the highest compression yield strength of 260 MPa and Vickers hardness of 104 HV. The Zn-5Er alloy shows a 126 MPa tensile yield strength, a 279 MPa ultimate tensile strength, 52% elongation, a 196 MPa compression yield strength, and a 101 HV Vickers microhardness. Further, the Zn-5Er alloy has a 130 µm per year corrosion rate in electrochemical tests and a 26 µm per year degradation rate in immersion tests, which is the lowest among the tested alloys. It also has the best in vitro osteogenic differentiation ability and capacity for osteogenesis and osteointegration in vivo after implantation in rat femurs among the Zn-5RE alloys, indicating promising potential in load-bearing biodegradable internal bone-fixation applications. Statement of significanceThis work reports the exceptional mechanical, corrosion, and biocompatibility properties of hot-extruded (HE) Zn-5 wt.%–rare earth (Zn-5RE) alloys using single yttrium (Y), holmium (Ho), and erbium (Er) alloying for biodegradable bone-implant applications. Our findings demonstrate that the HE Zn-5Er alloy showed σuts of 279 MPa, tensile yield strength of 126 MPa, elongation of 51.6%, compression yield strength of 196 MPa, and microhardness of 101.2 HV. Further, HE Zn-5Er showed the lowest electrochemical corrosion rate of 130 µm/y and lowest degradation rate of 26 µm/y, and the highest in vitro osteogenic differentiation ability, in vivo osteogenesis, and osteointegration ability after implantation in rat femurs among the Zn-5RE alloys, indicating promising potential in load-bearing biodegradable internal bone-fixation applications.