Abstract
A selective laser melted Al-4.5Mg-0.6Sc-0.3Zr alloy, also known as Scalmalloy®, was cold-rolled at two different reductions in thickness to observe the effect on microstructure and mechanical properties. Optical microscopy, scanning electron microscopy, tensile testing with digital image correlation, surface roughness testing and microhardness testing was used to examine samples. Hardness increased significantly in the 30% cold-rolled condition – 20.2% in the horizontal plane, 12.5% in the transverse plane, and 18.2% in the longitudinal plane. Surface roughness was reduced to as low as 1.2μm for cold-rolled conditions compared to >15μm for as-built conditions. Yield strengths were less for cold-rolled conditions compared to as-built and ultimate tensile strengths were similar for as-built and 10% cold rolled conditions. However, 30% cold-rolled condition saw a 10.8% increase compared to as built. Strain distribution among samples was uniform for as-built conditions but concentrated in certain areas for cold-rolled conditions. SEM micrographs of fracture surfaces showed some very ductile fractures evident from dimpling. The microstructure was heavily deformed for all cold-rolled conditions in all build directions showing flattened, elongated grains and grain refinement in both the coarse grain and fine grain regions present in Scalmalloy, especially for the 30% cold-rolled condition.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.