Abstract
A continuous γ/γ′ two-phase field has been identified extending between the ternary Co–Al–W system to the binary Co–Ti system. The lattice misfits of two phase γ/γ′ alloys from the Co–Al–W–Ti quaternary system were measured by X-ray diffraction and found to be positive and vary linearly with composition. Differential scanning calorimetry measurements showed that the solidus and liquidus temperatures decrease from the W and Al rich end to the Ti rich end, whilst the γ′ solvus temperature increases. Long term heat treatments identified the occurrence of discontinuous precipitation at the grain boundaries in many of the alloys studied. The high temperature strength and creep resistance of the quaternary alloys in the intermediate composition range surpassed those of the binary and ternary alloys.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.