Abstract
Comparative investigations on the microstructures, thermal stability and mechanical properties of Mg 77Cu 12Zn 5Y 6 and Mg 77Ni 12Zn 5Y 6 bulk metallic glass matrix composites were carried out by using scanning electron microscopy (SEM), DSC and compressive tester. The results show that the microstructure of as-cast samples with 3 mm in diameter for Cu-containing alloy is consisted of Mg flakes and dotted Mg 2Cu phase in the amorphous matrix, while the as-cast Ni-containing alloy with the same diameter is mainly consisted of Mg flakes in the amorphous matrix. The glass transition temperature and supercooled liquid region are 413 K and 27 K for the Cu-containing, 443 K and 32 K for the Ni-containing amorphous matrix composites, respectively. The fracture strength, yield strength and plastic strain are 532 MPa, 390 MPa and 2.4% for the Cu-containing alloy, 667 MPa, 412 MPa and 7% for the Ni-containing alloy, respectively. Furthermore, the fracture mechanism for the amorphous matrix composites was discussed according to both the fracture surfaces and the stress–strain curves.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.