Abstract
The effect of 20-keV Ar+ ion irradiation on the mechanical properties andfatigue resistance of 6 mm thick hot-extruded profiles made of a D16 alloy (Al–Cu–Mg system) has been studied after natural aging. Irradiation at fluences of 2.1015 cm−2 and 1.1016 cm−2 has been revealed to increase the number of cycles to failure significantly at low load amplitudes σ/σu = 0.3. The maximum increase in the number of cycles to destruction 2.4 times is observed at a smaller fluence of ions F = 2.1015 cm−2.