Mechanical properties and fatigue life detection of copper particle filled polyester composite material under rotating bending load
Highlights
A composite material could be a combination of two materials with diverse chemical and physical properties
Many researchers have been investigated the Mechanical behaviour of composite materials such as, Antunes F.V. et al [3] predicted the fatigue life of three particles polymer composites with various particles sizes and various filler volume fractions
The composite materials were kept in the mold for 24 hours to cure at room temperature, the product of tensile and fatigue specimens were left in the oven at 70oC for 3 hours in order to achieve a sufficient curing process [17]
Summary
A composite material could be a combination of two materials with diverse chemical and physical properties. As well as, enhancing some mechanical characteristic of material such as stiffness and tensile strength. The preference of composite material comes from the enhancing of base material’s properties and wide range of application in the industries [1]. A reinforcement composite could be a particle with various dimensions generally equal are called particulate strengthened composites. A particulate reinforcement not generally leads to strengthen but enhance the stiffness [2]. Many researchers have been investigated the Mechanical behaviour of composite materials such as, Antunes F.V. et al [3] predicted the fatigue life of three particles polymer composites with various particles sizes and various filler volume fractions. The fracture mechanics approach was used to obtain stress intensity factor for central hole specimens and compare the theoretical and experiment result
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.