Abstract
Alumina microlattices with solid struts and different topologies were fabricated by the stereolithography 3D printing method. Mechanical analysis shows that specific stiffness and strength were highest for Simple Cubic lattices, followed by Octet Truss, then Kelvin Cell lattices. The mechanical properties followed Ashby's power law well at small relative densities (≤ 0.3), but deviated from it at higher relative densities due to the increased importance of joint deformation. Failure in the Simple Cubic lattices proceeded in a column-by-column manner from the boundaries inwards to the centre, while fracture in Octet Truss and Kelvin Cell lattices took place predominantly along the diagonal (111) and (110) planes respectively. The underlying mechanism controlling these mechanical responses has been thoroughly discussed using finite element simulation analysis. Because lattice strength was limited by the tensile strength of alumina, which was an order of magnitude lower than its compressive strength, the microlattices were weaker than Ashby's predictions. Nevertheless, they were still able to exhibit better specific modulus and strength than many current engineering materials, as well as some degree of ductility in the form of pseudoplastic strains (0.1 % - 0.5 %).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.