Abstract
The effects of La content on the mechanical properties and corrosion behavior of as-cast Mg-Zn-Zr (ZK) magnesium alloys were investigated. The results showed that La addition to ZK60 alloy resulted in a considerable grain refinement and an increase in the volume fraction of second phases by formation of Mg-Zn-La ternary phase. The tensile tests were performed at both room and elevated temperatures. At room temperature, the yield and tensile strengths and elongation-to-fracture significantly increased with 0.2 wt.% La addition, then deteriorated slightly with increasing La additions above 0.2 wt.%. At 200 °C, the yield and tensile strengths continually improved and elongation-to-fracture decreased with increasing La content due to the presence of thermally stable Mg-Zn-La phase. Immersion and electrochemical corrosion tests revealed that the formation of Mg-Zn-La phases led to a higher amount of cathodic sites and preferential corrosion propagation, and thus a decrease in the corrosion resistance of ZK60 alloys.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.