Mechanical Properties and Bond Strength of Additively Manufactured and Milled Dental Zirconia: A Pilot Study.

Abstract

To evaluate and compare the mechanical properties and ceramic bond of additively manufactured and milled dental zirconia materials. Disc (r = 10mm, h = 2mm) and bar (25 4 × 1. 2mm) shaped milled (M group) (Nacera Pearl; Doceram) and additively manufactured (AM group) (NanoParticle Jetting; XJet, Carmel 1400) zirconia specimens were prepared for 2 experimental groups. Ceramic was applied to the disc specimens (h = 4mm, r = 6mm) (n = 9) and their shear bond strength (SBS) was measured. The surface morphology of disc specimens was analyzed with a scanning electron microscope (SEM). The Vickers microhardness (Vh), surface roughness (Ra), and three-point flexural strength (FS) of bar specimens (n = 9) were measured. Results were statistically analyzed with Mann-Whitney U-test (α = 0.05). Significant differences were found in FS and Vh values of the M and AM groups. M group (1501.4 ± 60.1 HV1) showed a significantly higher Vh value than the AM group (1169.2 ± 48.4 HV1) (p < 0.001). FS of the M group (1287.5 ± 115.2 MPa) exhibited significantly high value than the AM (1030.0 ± 29.2 Mpa) group (p < 0.001). Statistically, no significant differences were seen in SBS and Ra values of the M and AM groups. Within the limitations of this in vitro study, the manufacturing technique affected the mechanical properties of the zirconia materials. AM zirconia material showed lower Vh and FS values than M zirconia. Additionally AM zirconia demonstrated adequate bond strength with dental ceramic.