Mechanical Performances of Phenolic Modified Epoxy Resins at Room and High Temperatures

Abstract

Epoxy is an important resin matrix and has been widely applied in laminated composites as a coating or adhesive material. In this article, the phenolic was applied to modify the mechanical properties of epoxy resin. The phenolic modified epoxy resins with various phenolic content were prepared via a polytetrafluoroethylene mould, and the phenolic modified epoxy-based plain woven laminated composites (PWLCs) were manufactured via vacuum assisted resin transfer method for further study of phenolic modified epoxy resins’ mechanical properties. The compression tests were performed perpendicularly to thickness at 2 mm/min to investigate the mechanical performances of phenolic modified epoxy resins and epoxy-based PWLCs. The results showed that the addition of phenolic into epoxy could improve the mechanical performances of epoxy resins and epoxy-based composites at room temperature, and the phenolic influenced epoxy-based PWLC more than epoxy matrix at room temperature. However, at high temperatures, the addition of phenolic decreased the mechanical performances of epoxy resins and epoxy-based composites, and the adverse effect of phenolic became more serious with the increase of phenolic content at high temperature. In addition, the thermogravimetric analyses were also conducted from 30 °C to 800 °C on phenolic modified epoxy resins and the results showed that the phenolic modified epoxy resin had an earlier loss in weight than unmodified epoxy resin. The earlier loss in weight meant that the addition of phenolic into epoxy resin led to the formation of unstable molecules at high temperature.