Mechanical, electrical and self-sensing properties of cementitious mortars containing short carbon fibers

Abstract

This paper is aimed at exploring mechanical, electrical and self-sensing properties of cement-based mortars through the addition of short carbon fibers, at different dosages (2%, 3%, 4% by weight of cement). Compression and bending tests on carbon fiber reinforced mortars (CFRM) were performed. The addition of carbon fibers showed to enhance the mortars’ flexural strength by increasing the fibers content, while no improvement was found in the compressive strength. Electrical resistivity of the CFRM, at different days of curing, was evaluated by AC impedance measurements, using two stainless steel wire meshes as electrodes. The electrical resistivity decreased with time, until reaching a constant value after about 60 days of curing. Carbon fibers were able to drastically reduce the mortar resistivity, up to values below 150 Ω cm. The effect of fibers dosage on the ability of the mortar to change its electrical resistivity when subjected to different stress states was also studied. The specimens were gradually loaded up to 50–60% of the maximum compressive strength, carrying out two loading/unloading cycles, while resistivity was measured using a conductivity meter. Depending on the fibers dosage and stress state within the material, CFRM resistivity changed with significant variations.