Abstract
The mechanical deformation by spherical indentation of both crystalline InP and GaAs was characterized using cross-sectional transmission electron microscopy (XTEM) and atomic force microscopy. All load–unload curves show a discontinuity (or “pop in”) during loading. Slip bands oriented along {111} planes are visible in XTEM micrographs from residual indentations in both materials and no evidence of any phase transformations was found. Higher load indentations (35 mN for InP and 50 mN for GaAs) also revealed subsurface cracking. In contrast no cracking was found beneath a 25 mN InP indent although the hardness and modulus data are almost identical to those of the cracked sample. The subsurface cracks are thought to be nucleated by high stress concentrations caused by dislocation pileup.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.