Abstract
small radius of curvature from 1.52.0 diameter ratio (DR) have been investigated. Our pipe material was low carbon steel (SA106Gr-B) having the chemical compositions of 0.3C, 0.29Mn, 0.4Cr, and 0.4Cu (mass%). The high cycle fatigue, microstructure, hardness, and residual stress of two bent sections ®extrados and intrados regions ®were compared with those of the raw material section. Low carbon steel pipes have better fatigue characteristics at the bent section than at the raw material section. The improvements in the fatigue strength of specimen resulted from grain refinement and phase transformation, while compressive residual stress at surface of bent pipe remained by thermo-mechanical processing can give better fatigue properties in fields. [doi:10.2320/matertrans.MF201123]
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.