Abstract
Friction stir welding (FSW) is restricted to non-safety–critical aerospace components because there is no reliable method for detecting kissing bonds (KB), which may have a significant effect on fatigue life. The effects of KB defects on the tensile and fatigue properties of 7475-T7351 friction stir welds were quantitatively evaluated with respect to a reference weld without any flaws and a base material. Various KB defects were investigated with the aim of determining the defect size that does not have a significant influence on the fatigue life of joined 6.35-mm-thick plates. A critical value for the KB geometry appears to be a depth of 0.3mm considering the influence on fatigue life for the investigated configurations. This paper also presents results from micromorphological analyses of the fatigue crack initiation from the KB and from the analysis of the weld cross-section microstructure.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.