Abstract
Cu-TiB2 nanocomposite powders were in situ synthesized by combining high-energy ball milling of Cu-Ti-B elemental powder mixtures as precursors and subsequent self-propagating high temperature synthesis (SHS). Cu-40wt.% TiB2 was produced after SHS reaction and then diluted by copper to obtain desired homogeneous composites with 2.5, 5 and 10wt.%TiB2. Spark plasma sintering (SPS) was used to inhibit grain growth and thereby obtain fully Cu-TiB2 sintered bodies with nanocomposite structure. After SHS reaction, only Cu and TiB2 phases were detected in the SHS-product. Spheroidal TiB2 particles smaller than 250nm were formed in the copper matrix after SHS-reaction. Mechanical and electrical properties were investigated after SPS at 650°C for 30min under 50MPa. The electrical conductivity decreased from 75 to 54% IACS with increasing of TiB2 contents from 2.5 to 10wt.%. However, hardness increased from 56 to 97HRB. In addition, the tensile strength increased with increasing the TiB2 content.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.