Mechanical behavior of facial prosthetic elastomers after outdoor weathering

Abstract

Objectives The degradation of maxillofacial prosthetic elastomers that occurs during physical weathering is usually responsible for the replacement of prostheses. In this study the mechanical behavior of 4 non-pigmented facial prosthetic elastomers, exposed to outdoor weathering for 1 year, was investigated. The hypothesis investigated was that irradiation time did not affect the properties measured. Methods The samples were exposed to solar radiation for 1 year in Thessaloniki (Greece). Three different types of polydimethyl siloxane (PDMS) and chlorinated polyethylene (CPE) samples were tested in this study. Mechanical tests (compressive-tensile) were performed using a universal type testing machine. Hardness tests were evaluated using a durometer tester. Simple mathematical models were developed to correlate the measured properties with irradiation time. The stress–strain data of compression and tensile tests were modeled using parameters such as maximum stress ( σ max), maximum strain ( ɛ max), elasticity parameter ( E), and non-linearity parameter ( p), while the mathematical model used for hardness data involves initial hardness of materials ( H 0). Results Two of the silicone prosthetics (Elastomer 42, TechSil 25) seem to become harder and more brittle contrary to the other silicone (M 511) and chlorinated polyethylene (CPE) samples that become softer and more ductile. Duration of exposure increases these phenomena. Conclusion The effect of irradiation time on the mechanical behavior was introduced through its effect on the models’ parameters. The hypothesis was rejected since changes were observed in the model parameters.