Abstract
Objective:This study aims to evaluate the effect of acidic solutions (AS) on surface roughness (Ra) and microhardness of restorative materials (RM).Materials and Methods:Eight volunteers wore intraoral palatal devices (IPD) containing samples of RM: Ketac Nano (KN); Ketac Nano + Biscover LV (KN-B); Esthet-X (EX); Esthet-X + Biscover LV (EX-B); Supreme XT (SXT); Supreme XT + Biscover LV (SXT-B); and bovine enamel. The samples were submitted to three phases: (1) immersion in 0.01M hydrochloric acid (HCl) – 10 min, three times/day (14 days); (2) immersion in soft drink (Sprite®) – 10 min, three times/day (14 days); and (3) keeping in saliva (14 days). Changes in Ra/microhardness were measured before/after the three phases.Statistical Analysis:ANOVA (α = 0.05) and Fisher's test.Results:Materials sealed with Biscover LV (B) presented lowest values in all periods. KN glass ionomer cement showed highest Ra values after exposure in AS. Application of B did not reduce the Ra for the composites studied, except for EX after immersion in HCl. AS promoted changes in Ra/microhardness of RM, except for sealed materials.Conclusions:The acids used were able to change the Ra and microhardness of RM, except of the sealed materials. The resin-modified GIC showed the most significant changes after immersion in AS; and the composites sealed with B, even after immersion in acidic solutions (AS), showed the lowest Ra values and the least degradation in microhardness, especially when subjected to low pH solutions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.