Abstract

The effect of adding gilsonite micrometric particles on the properties of N330 carbon black (CB) reinforced natural rubber (NR) compounds was investigated. Formulations with 30/0, 22.5/7.5, 15/15, 7.5/22.5 and 0/30 parts per hundred of rubber (phr) of CB/gilsonite were used, comparing the effect of conventional and efficient vulcanization systems. Gilsonite was characterized by X-ray fluorescence (XRF), thermogravimetric analysis (TGA), elemental analysis, X-ray diffraction (XRD) and scanning electron microscopy (SEM). Tension, uniaxial compression, compression-set, abrasion resistance and dielectric strength tests were carried out on specimens that were moulded using the optimal curing time measured by oscillating disc rheometry (ODR). Abrasion wear resistance, and mechanical and rheometric properties varied with the CB/gilsonite content and on the vulcanization system. It was found that gilsonite facilitated the incorporation of carbon black during mixing, diminished the reversion during rheometric tests of compounds with efficient vulcanization cure systems and increased the dielectric strength. Some gilsonite/CB/NR compounds showed similar rheometric properties, compressive modulus and wear resistance to CB/NR compounds, which evidenced the use of gilsonite as an available filler for NR-based materials.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.