Abstract
In this work, Gas Metal Arc Welding (GMAW) was used to study the influence of heat input (i.e. cooling rate) on mechanical/metallurgical properties of square butt welded joints of DP 1000 sheets. The influence of filler metals of different strengths on the mechanical properties of joints was also tested. A significant decrease in hardness was observed in the Heat Affected Zone (HAZ) due to martensite tempering, in regions where peak temperature was close to isotherm AC1 (calculated in 735 oC for these steel); coincidently, fracture in every tensile test occurred in regions where martensite was tempered, even when a wire of less strength was used. It was noticed that the decrease in ultimate tensile and yield strength of base metal was inherent to welding. When minimum heat input was used, deterioration in mechanical properties was less pronounced, once degree of HAZ softening was smaller. Elongation of joints increased with increasing heat input.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Engineering & Technology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.