Mechanical and electrical properties of radiation-vulcanized natural rubber latex with waste eggshell powder as bio-fillers

Abstract

ABSTRACTThis work investigated the mechanical, physical, morphological, and electrical (volume) resistivity properties of radiation-vulcanized natural rubber latex (RVNRL) with additions of waste eggshell (WES) powder, which contained primarily CaCO3 (calcite). The results showed that increasing gamma irradiation doses from 0 to 30 kGy in 10-kGy increments led to decreases in the swelling ratio and elongation at break but increases in the crosslink density, tensile modulus at 500% elongation, and tensile strength of the composites. The results also suggested that increasing the WES contents from 0 to 2, 4, or 6 parts per hundred parts of rubber by weight (phr) in the composites improved the tensile modulus at 500% elongation, tensile strength, hardness (Shore A), and electrical (volume) resistivity. In addition, after undergoing thermal aging at 70°C for 96 h, the tensile modulus and hardness (Shore A) increased, while the tensile strength and elongation at break decreased. This work also compared the properties of WES/RVNRL with commercial CaCO3/RVNRL samples at the same 4-phr content. The results indicated that both composites had similar tensile properties, implying possible replacement of commercial CaCO3 with WES powder as an effective reinforcing filler in RVNRL.