Mechanical and barrier properties of polyvinyl chloride plasticized with dioctyl phthalate, epoxidized soybean oil, and epoxidized cardanol

Abstract

AbstractPlasticized polyvinyl chloride (PVC) films were prepared by melt compounding and compression molding using epoxidized cardanol (EC), a biobased plasticizer and its plasticization effect was compared with epoxidized soybean oil (ESBO) and dioctyl phthalate (DOP). The mechanical, migration, thermal, and barrier properties of the plasticized films were compared. The effect of replacing DOP with EC on the properties of PVC films was also investigated. The tensile strength, elongation at break, tensile modulus and impact strength values of PVC/EC films were higher in comparison to PVC/DOP and PVC/ESBO films at a fixed plasticizer loading of 40 wt.%. Also, the films prepared with a mixture of DOP + EC showed higher tensile strength and elongation at break compared to that of films prepared with only DOP. The PVC/EC films showed good thermal stability and reduced oxygen transmission rate (OTR) compared to PVC/DOP films. The addition of graphene and nanoclay in the PVC/plasticizer system exhibited an increase in oxygen transmission. However, the oxygen barrier property of nano filler incorporated PVC/EC films was better than PVC/DOP films. All the films showed negligible water vapor transmission rate (WVTR).