Abstract
Changes in MgH2 decomposition kinetics were investigated in dependence on complex doping of MgH2 by Al, Ti, Ni, and Fe. Reactive mechanochemical alloying method (RMA) was applied in the temperature descending regime. It was found that addition of Al+Ni+Ti, Al+Ti, Fe+Ti (see below) and Al+Fe elements combinations led to a lower thermal stability and, consequently, to a lowering of the temperature of hydrogen desorption onset. Whereas desorption began at temperature of 320 °C from the pure MgH2, the aditions of Al, Ni, Ti and Fe lowered the start of the desorption down to 250°C (at hydrogen pressure 0.1 MPa in the reactor). Very fast desorption kineticsprecize at 300 0C and PH 2= 0.1 MPa were observed for Mg+Me mixture in comparison with the pure Mg. Sorption capacity of investigated mechanically-alloyed composites varied from 5 to 6.5 wt. % H2. The tested materials showed a high potential as hydrogen storage alloys especially for stationary application.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.