Mechanical alloying and self-propagating high-temperature synthesis of stable icosahedral quasicrystals

Abstract

Abstract The phase evolution of the mechanically alloyed ternary 63%Al + 25%Cu + 12%Fe and 65%Al + 20%Cu + 15%Fe powder mixtures with milling time has been studied by X-ray diffraction method. It was found that an icosahedral quasicrystalline phase was formed directly during high-energy ball milling of the Al–Cu–Fe mixtures. The X-ray and scanning electron microscopic investigations demonstrated the possibility to use self-propagating high-temperature synthesis (SHS) in combination with preliminary mechanical activation for the synthesis of stable icosahedral quasicrystals. The typical morphology of the Al 63 Cu 25 Fe 12 icosahedral quasicrystals formed in the SHS process is a pentagonal dodecahedron with a size of 3–5 mm. The phase composition of the SHS products depends on the time of preliminary mechanical activation. The content of cubic intermetallic phase in SHS products increases with the time of preliminary mechanical activation of the 63%Al + 25%Cu + 12%Fe powder mixtures.