Abstract
Thermal degradation of two polyol ester lubricants with the same base chemical structures from two different manufacturers at high temperature (i.e., 220 °C) has been studied. Gel permeation chromatography was used to identify the high molecular weight products formed during thermal stressing of these lubricants. The amount of high molecular weight products generated at different stages of the degradation (e.g., dimers, oligomers) was quantified. Several other techniques were utilized as a combined analytical approach to provide comprehensive measurement of lubricant degradation in the liquid phase. The mechanism of degradation and the formation of oxidation products have been presented. A significant difference in the extent of degradation of the two lubricants was observed using different analytical techniques.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.