Measurements on Subscale Y-Ba-Cu-O Racetrack Coils at 77 K and Self-Field

Abstract

YBa <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> Cu <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">7-¿</sub> (YBCO) tapes carry significant amount of current at fields beyond the limit of Nb-based conductors. This makes the YBCO tapes a possible conductor candidate for insert magnets to increase the bore field of Nb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> Sn high-field dipoles. As an initial step of the YBCO insert technology development, two subscale racetrack coils were wound using Kapton-insulated commercial YBCO tapes. Both coils had two layers; one had 3 turns in each layer and the other 10 turns. The coils were supported by G10 side rails and waxed strips and not impregnated. The critical current of the coils was measured at 77 K and self-field. A 2D model considering the magnetic-field dependence of the critical current was used to estimate the expected critical current. The measured results show that both coils reached 80%-95% of the expected values, indicating the feasibility of the design concept and fabrication process.