Abstract
Aluminum (Al) is a convenient proxy for beryllium (Be) plasma material interaction studies since they have a number of physical and chemical similarities. Al samples were exposed at the lower outer strike point of an L-mode divertor plasma in DIII-D (conditions 7–11×1018 D-ions cm−2s−1, Te=12–47eV). The gross erosion rate was directly measured using post-mortem ion beam analysis of small 1mm-sized samples where local re-deposition was determined to be negligible. The gross erosion rate was also calculated using spectroscopic methods, but these rates greatly underestimate the direct (i.e. non-spectroscopic) measurement. The direct measured erosion yields were within the range of published D+→Al ion beam sputtering yields. The ionizations per photon (S/XB) coefficients used in the spectroscopic analysis were determined in separate experiments using He plasmas at the PISCES-B linear plasma facility at UCSD. The measured S/XB coefficients were on average ∼6× higher than the theoretically calculated values.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.