Measurement of Thin-film Coating Hardness in the Presence of Contamination and Roughness: Implications for Tribology

Abstract

Standard nanoindentation measurements on commercially available TiAlN, CrN, metal-containing diamond-like carbon, and TiN coatings, deposited on steel substrates were performed to determine coating hardness and elastic modulus. It was found that the coating surface roughness/morphology present after deposition can significantly affect the measurements of nanomechanical properties so that measurements of these properties on the as-deposited coating surface may be significantly different from the bulk. In addition, a surface measurement may produce a lower nanohardness due to the existence of a soft surface contamination layer. A simple method was developed to enable accurate measurement of the nanomechanical properties of coatings, while avoiding errors introduced by surface topography and the presence of superficial contamination layers on thin films. Friction and wear behavior, as well as the wear mechanisms in dry reciprocating sliding contact of the various coatings with a steel ball can be correlated to the surface attributes of each coating in terms of roughness and the presence of contamination layers, both of which are shown to also affect the nanohardness measurements.