Abstract
The internal tensile stresses in Co68.2Fe4.3Cr3.5Si13B11 glass-coated amorphous microwires are measured experimentally by using the stress sensitivity of saturation magnetostriction. The obtained results show that the internal tensile stress is 1420MPa for microwire with metallic core diameter of 20.7µm and glass cover thickness of 14.5µm, while it decreases to 640MPa after glass removal. The measured results agree well with the theoretical results calculated by Chiriac et al.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.