Abstract
The capability of growing state-of-the-art middle wavelength infrared (MWIR)-HgCdTe layers by molecular beam epitaxy (MBE) on large area silicon substrates has been demonstrated. We have obtained excellent compositional uniformity with standard deviation of 0.001 with mean composition of 0.321 across 1.5″ radii. R0A as high as 5 × 107 ω-cm2 with a mean value of 7 × 106 Θ-cm2 was measured for cut-off wavelength of 4.8 µm at 77K. Devices exhibit diffusion limited performance for temperatures above 95K. Quantum efficiencies up to 63% were observed (with no anti-reflection coating) for cut-off wavelength (4.8–5.4) µm @ 77K. Excellent performance of the fabricated photodiodes on MBE HgCdTe/CdTe/Si reflects on the overall quality of the grown material in the MWIR region.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.