Abstract
We report the elongation of embedded Au nanoparticles (NPs) in three different matrices, i.e. amorphous carbon (a-C), crystalline indium tin oxide (InxSn1-xOz; ITO) and crystalline calcium fluoride (CaF2), under irradiations of 4 MeV C60+ cluster ions and 200 MeV Xe14+ ions. Under 4 MeV C60 cluster irradiation, strong sputtering is induced in CaF2 layer so that the whole the layer was completely lost at a fluence of 5 × 1013 ions cm−2. Au NPs were partly observed in the SiO2, probably due to the recoil implantation. Amorphous carbon (a-C) layer exhibits low sputtering loss even under 4 MeV C60 irradiation. However, the elongation in a-C layer was low. While the ITO layer showed a certain decrease in thickness under 4 MeV C60 irradiation, large elongation of Au NPs was observed under both 4 MeV C60 and 200 MeV Xe irradiation. The ITO layer preserved the crystallinity even after large elongation was induced. This is the first report of the elongation of metal NPs in a crystalline matrix.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.