Abstract
Cadmium zinc telluride (Cd1−x ZnxTe or CZT) has shown great promise as a material for room temperature x-ray and gamma-ray detectors. In particular, polycrystalline material grown by the high pressure Bridgman method with nominal Zn fraction (x) from 0.1 to 0.2 has been used to fabricate high resolution gamma-ray spectrometers with resolution approaching that of cooled high-purity Ge. For increased sensitivity, large areas (> 1 cm2) are required, and for good sensitivity to high energy gamma photons, thick detectors (on the order of 1 cm) are required. Thus, there has been a push for the development of CZT detectors with a volume greater than 1 cm3. However, nonuniformities in the material over this scale degrade the performance of the detectors. Variations in the zinc fraction, and thus the bandgap, and changes in the impurity distributions, both of which arise from the selective segregation of elements during crystal growth, result in spectral distortions. In this work, several materials characterization techniques were combined with detector evaluations to determine the materials properties limiting detector performance. Materials measurements were performed on detectors found to have differing performance. Measurements conducted include infrared transmission, particle induced x-ray emission, photoluminescence, and triaxial x-ray diffraction. To varying degrees, these measurements reveal that “poor-performance” detectors exhibit higher nonuniformities than “spectrometer-grade” detectors. This is reasonable, as regions of CZT material with different properties will give different localized spectral responses, which combine to result in a degraded spectrum for the total device.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have