Abstract

Linepipes installed in permafrost ground or seismic region, where larger strains can be expected by ground movement, are required to have sufficient strain capacity in order to prevent local buckling or girth weld fracture. On the other hand, strain capacity of linepipes usually degreases with increasing strength, and this is one of the reasons for preventing wider use of high-grade linepipe for high strain application. Furthermore, external coating is necessary for corrosion resistance of pipe, but coating heat can cause strain-aged hardening, which results in increased yield strength and Y/T. Therefore, there is a strong demand for developing high strength linepipe for a high strain application with resistance to strain-aged hardening. Extensive studies to develop Grade X100 high strain linepipe have been conducted. One of the key technologies for improving strain capacity is dual-phase microstructural control. Steel plate with the microstructure including bainite and dispersed martensite-austenite constituent (MA) can be obtained by applying accelerated cooling followed by heat treatment online process (HOP). HOP is the induction heating process that enables rapid heating of the steel plates. Variety of microstructural control, such as fine carbide precipitation and MA formation, can be utilized by this newly developed heating process. One of the significant features of the HOP process is to improve resistance to strain-aged hardening. Increase in yield strength by coating can be minimized even for the Grade X100 linepipe. Trial production of X100 high strain linepipe with the size of 36″ OD and 15mm WT was conducted by applying the HOP process. Microstructural characteristics and mechanical properties of developed X100 linepipe are introduced in this paper. In order to evaluate compressive strain capacity of the developed pipe, full-scale pipe bending test was carried out by using the trial X100 high strain linepipe after external coating. Full scale bending test of developed X100 linepipe demonstrated sufficient compressive strain capacity even after external coating.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.