Abstract

This study experimentally investigates the influence of several material parameters on steel fiber reinforced concrete (SFRC) structural beams and their crack-bridging degradation over constant and variable amplitudes of flexural cyclic loading. Crack-bridging stress is evaluated using inverse analysis and its degradation against maximum rebars strain is derived. Four series of SRFC beams are prepared and characterized with different concrete compressive strengths, hooked-end steel fiber shapes in two different volume fractions, and two longitudinal reinforcement ratios. The results reveal lower crack-bridging degradation rates, and associated longer fatigue life and higher residual capacity, for beams with higher concrete strength. Further, SFRC fracture energy is shown to have a significant effect on fatigue response, with higher fracture energy associated with lower rates of crack-bridging degradation. However, steel fibers with double hooks are shown to have a relatively insignificant effect on controlling crack-bridging degradation rates and the flexural cyclic responses of SFRC beams as compared to single hook fibers. Also demonstrated is that a lower longitudinal reinforcement ratio leads to higher rebar strain rates with no influence on crack-bridging stress. Crack-bridging degradation diagrams are proposed for SFRC beams that quantitatively capture several material parameters effects based on their mechanical properties over the fatigue life.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.