Abstract
For Ru and Ir oxide electrodes sintered at different temperatures, in this work, surface resistivity, X-ray photoelectron spectroscopy, electrode lifetime, voltammetric charge capacity, and total organic carbon of 4-chlorophenol (4CP) decomposition at the electrodes were measured, and then intermediates during the electrolysis were identified by gas chromatography-mass spectroscopy to predict the destruction path of 4CP at the electrodes. A sintering temperature of around 650°C, rather than 400-550°C suggested in the literature for the fabrication of Ru and Ir oxide electrode, showed the highest organic destruction yield. The sintering temperature strongly affected the electrode lifetime as well. During the high temperature sintering, increase of the sintering time caused the oxidation of the Ti substrate to result in the increase of oxide weight of the electrode and the solid diffusion of the generated to the electrode surface, which decreased the electrode activity so that the organic destruction yield went down slowly. The destruction path of 4CP at a high temperature-sintered electrode was suggested to be different from that at a low temperature-sintered one. The Ru oxide electrode sintered at 450°C generated several complicated aliphatic intermediates. © 2002 The Electrochemical Society. All rights reserved.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.