Mass Spectroscopy of Neutral Metal Oxide Clusters Using a Desk-Top Soft X-Ray Laser

Abstract

We report the use of a compact 46.9 nm capillary discharge soft x-ray laser in the study of metal-oxide nanoclusters using mass spectroscopy. Transition metal oxides are widely used as heterogeneous catalysts and catalytic supports in industrial processes. There are numerous applications for transition metal oxide catalysts, and although they are widely used, there is a lack of fundamental understanding of the complicated processes that occur on the metal oxide surface during catalysis. Conventional nanocluster spectroscopy techniques have used 193 nm radiation from an ArF excimer laser corresponding to a photon energy of 6.4 eV in order to photoionize a sample. Typical metal oxide nanocluster ionization energies fall into the range of 7-12 eV while some have even higher energies. Therefore a single 6.4 eV photon can not ionize the cluster making multiphoton processes the dominant ionization method. A major problem associated with mass spectroscopy can become evident during the multiphoton ionization of clusters. Specifically, the clusters may fragment during the ionization process and the identification of the neutral parent cluster can become difficult. In the present experiment neutral vanadium, niobium and tantalum oxide clusters are studied by single photon ionization with the 26.5 eV photons produced by a capillary discharge soft x-ray laser.1 During ionization, the metal oxide clusters are observed to be almost free of serious fragmentation. The most stable neutral cluster of vanadium, niobium, and tantalum oxide growth in a saturated oxygen condition are identified as MO2, M2O4/M2O5, M3O7, M4O10, M5O12, M6O15, M7O17, M8O20, and M9O22, which can be represented as a form (MO2)0,1(M2O5)y. M2O5 is identified as a basic unit to build-up the three kinds of metal oxide clusters. In the case of niobium and tantalum oxide clusters, the oxygen-deficient clusters with a structure of (MO2)2(M2O5)y are detected for groups that contain an even number of metal atoms. For vanadium oxide clusters, the oxygen-deficient clusters are detected for every family, indicating a stable structure of (VO2)x(V2O5)y. The stoichiometry of oxygen-rich clusters can be expressed as (MO2)0,1(M2O5)yO1-3 and their structures are consistent with chemically bonded species.