Masking ability of implant abutment substrates by using different ceramic restorative systems

Abstract

Statement of problemInformation regarding the masking ability of ceramic crowns over different implant abutment materials is scarce. PurposeThe purpose of this in vitro study was to evaluate the masking ability of different monolithic or bilayer ceramic materials with different thicknesses over substrates indicated for implant restorations by using opaque and translucent evaluation pastes. Material and methodsDisk-shaped specimens, shade A1 (VITA Classic; Ø10×1.5 to 2.5 mm), of different ceramics (a bilayer system [yttria-stabilized zirconia infrastructure+porcelain veneer: Zir+Pc] and monolithic systems [lithium disilicate under low, medium, or high translucency: LtLD, MtLD, or HtLD, respectively, and a high-translucent yttria-stabilized zirconia: HtZir]) were made (n=4). The color difference (ΔE00) was assessed by using the CIEDE2000 formula and considering the different ceramic systems over 5 implant abutment materials (A1 shade Zir [Zir A1]; white Zir [White Zir]; A1 low-translucency lithium disilicate [LD]; polyetheretherketone [PEEK]; and titanium [Ti]) when using 2 different evaluation pastes (translucent or opaque). The control comparison was the restorative material positioned over the Zir A1 substrate with a translucent evaluation paste. Statistical analysis was made by using a 2-way ANOVA and Tukey post hoc tests (α=.05) for ΔE00 data considering the restorative material and luting agent factors as their association. Additionally, ΔE00 data were qualitatively analyzed considering the acceptability and perceptibility thresholds. The translucency parameter (TP00) of each restorative material was evaluated, and data were submitted to 1-way ANOVA and Tukey post hoc tests (α=.05). ResultsThe most predictable masking ability was seen with Zir+Pc regardless of the evaluation paste used. Nevertheless, under 1.5-mm thickness, Zir+Pc did not adequately mask Ti (ΔE00>1.77). Most monolithic ceramics did not mask discolored substrates (PEEK or Ti, ΔE00>1.77). The exception was HtZir, which presented acceptable masking ability over PEEK at 2.5-mm thickness with both evaluation pastes (ΔE00<1.77). Regardless of the restorative material thickness, Zir+Pc showed the lowest (P<.05) TP00 values (TP00=3.45 at 1.5-mm thickness; TP00=2.00 at 2.5-mm thickness), and HtLD presented the highest (P<.05, TP00=23.50 at 1.5-mm thickness; TP00=13.36 at 2.5-mm thickness). HtZir showed similar TP00 to MtLD at 1.5-mm thickness and similar TP00 to Zir+Pc when used at 2.5-mm thickness (P>.05). ConclusionsMonolithic ceramics should be used with caution over discolored implant abutments. Bilayer systems (Zir+Pc) were the most predictable approach to adequately masking discolored substrates such as PEEK or Ti. An increased restoration thickness provided higher masking ability for all restorative materials tested.