Abstract
Cu-Al-Ni alloys, similarly as other Cu-base shape memory alloys, transform into more martensitic structures α 1 ' (6R), β 1 ' (18R) and γ 1 ' (2H), depending on the temperature, stress, load axis orientation, sense of loading and composition. The transformation stress-temperature conditions at which individual transitions take place are beneficially represented in so called non-equilibrium stress-temperature phase diagrams. On the basis of the σ-T diagrams, complex history dependent thermomechanical behaviors of SMA single crystals undergoing sequentially multiple solid state transitions can be easily understood and predicted. Since chemical composition of the alloy crystals affects mainly the equilibrium transformation temperatures, To, and only slightly the slopes of the transformation lines in the σ-T diagrams, the diagrams mainly shift in the temperature range (over ∼200K) with the compositional variations. The shape of the diagrams, however, may change significantly when the To shifts for individual transitions are different. Knowledge of the compositional dependence of σ-T diagrams would be beneficial for the development of shape memory alloys with specific required thermomechanical properties. The aim of the present work is experimental investigation of the martensitic transformations and construction of the σ-T diagram for Cu-Al-Ni alloy with lower Al content (To>363K) and comparison with our previous results obtained on alloys with higher Al content (T 0 <263K).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.