Abstract
Martensitic transformations in the Fe-(24-30)Ni-(5-8)Si (mass%) alloys have been investigated by means of optical and transmission electron microscopy, differential scanning calorimetry and hardness-testing. The Ms temperature is decreased by Si addition and the morphology of martensite is mainly lenticular in the unaged specimens. However, a pronounced decrease in the Ms temperature and a change in the martensite morphology from the lenticular to the thin plate type are observed on ausaging at 400°C. The increase in austenite hardness, the decrease in the Ms temperature and the increase in the tetragonality of martensite after ausaging at 400°C are clarified as due to the formation of nanoscale particles of γ'-(Ni,Fe) 3 Si with the L12 structure during ausaging at 400°C. The Fe-Ni-Si alloys that form thin plate martensite show the shape memory effect, which arises from the reverse transformation of stress-induced martensite to austenite. Precipitation hardening of the austenite phase by fine y' particles during ausaging improves the degree of shape recovery.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.